1.4466 UREA 25.22.2 310MoLN duplex steel S31050 bars and rods
Introduction
HT PIPE company supplies high quality 310MoLN bars.
Stainless steel grade 310MoLN is a fully austenitic stainless steel that does not have intermetallic phases such as intergranular carbide precipitations. The 310MoLN steel grade has an optimized chemical composition designed specifically for applications in urea plants. The nitrogen in the chemical composition helps to stabilize and strengthen the austenitic phase. This material provides improved corrosion-resistance in urea carbamate environments such as high-pressure strippers.
Density: 7.9g/cm3
Character
- Very good corrosion resistance to carbamide synthesis.
- Good corrosion resistance to intergranular corrosion.
Application
Production of carbamide.
Equal grades
UNS S31050, EN 1.4466, 00Cr25Ni20Mo2N, 25-22-2, X1CrNiMoN25-22-2
Chemical Composition
The chemical composition of stainless steel grade 310 MoLN is outlined in the following table.
Element |
Content (%) |
Iron, Fe |
Balance |
Chromium, Cr |
24-26 |
Nickel, Ni |
21-23 |
Molybdenum, Mo |
2-2.50 |
Manganese, Mn |
≤ 2 |
Nitrogen, N |
0.10-0.16 |
Silicon, Si |
≤ 0.70 |
Phosphorous, P |
0.025 |
Carbon, C |
≤ 0.020 |
Sulfur, S |
≤ 0.010 |
Mechanical Properties
The mechanical properties of stainless steel grade 310 MoLN are displayed in the following table.
Properties |
Metric |
Imperial |
Tensile strength |
540-740 MPa |
78320- 107327 psi |
Proof strength |
250 MPa |
36259 psi |
Modulus of elasticity (20°C) |
195 GPa |
28282 ksi |
Elongation at break (In 2", 50% cold worked) |
40% |
40% |
Hardness, Brinell |
95 |
95 |
Standards
- ASTM A240 Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
- ASTM A182-A182M-13 Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service
Product forms available
Bar, plate, sheet, tube, forging