acero inoxidable 2205 ficha tecnica ASTM A240 S31803 tubos y tuberias

Higher chromium, molybdenum and nitrogen content results in a Pitting Resistance Equivalent Number (PREN) > 40, providing superior pitting and crevice corrosion capabilities to austenitic and duplex stainless steels in virtually all corrosive media, and critical pitting temperature Above 50¡ãC .

It is widely used in offshore oil and gas exploration/production and in heat exchangers in petrochemical/chemical processing.

Super Duplex UNS S32750 bar has excellent resistance to stress corrosion cracking in chlorine containing environments. After heating to a solution treatment temperature of 1080¡ãC to 1120¡ãC, quenching is required.

The flange is second most used joining method after selding. Flanges are used when joints need dismantling. It provides flexibility for maintenance. Flange connects the pipe with various equipment and valves. Breakup flanges are added in the pipeline system if regular maintenance in required during plant operation.
A flanged joint is composed of three separate and independent although interrdlated components; the flanges, the gaskets, and the bolting; which are assembled by yet another influence, the fitter. Special controls are required in the selection and application of all there elements to attain a joint, which has acceptable leak tightness.
A flange is a protruded ridge, lip or rim, either external or internal, that serves to increase strength (as the flange of an iron beam such as an I-beam or a T-beam); for easy attachment/transfer of contact force with another object (as the flange on the end of a pipe, steam cylinder, etc., or on the lens mount of a camera); or for stabilizing and guiding the movements of a machine or its parts (as the inside flange of a rail car or tram wheel, which keep the wheels from running off the rails). The term “flange” is also used for a kind of tool used to form flanges.

The dual phase steel / super duplex steel stainless steel pipe is a kind of stainless steel with high strength and high corrosion resistance, which has the properties of austenitic stainless steel and ferritic stainless steel. Generally, when the carbon content is low, the Cr content is 18% ~ 28%, and the Ni content is 3% ~ 10%. Some steels also contain Mo, Cu, Nb, Ti, N and other alloy elements.
Type “Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size “OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”

Duplex 2205 stainless steels are called “duplex” because they have a two-phase microstructure consisting of ferritic and austenitic stainless steel grains. When duplex stainless steel melts, it solidifies from the liquid phase to a fully ferritic structure. As the material cools to room temperature, about half of the ferrite grains transform into austenite grains (“islands”). The result is a microstructure of approximately 50% austenite and 50% ferrite.

2507 has a higher chromium and molybdenum content which gives the super duplex greater corrosion resistance than other standard duplex grades.

The material has high strength and corrosion resistance. The A182 F53 material is used to make flanges ranging from 1/2 inches to 48 inches under different standards such as ANSI, ASME, DIN and other international standards.

Technically, the microstructure of a duplex 2205 tube is approximately 50% ferrite and 50% austenite. As a result, the properties inherited from both categories make this nitrogen-enhanced duplex 2205 seamless pipe ideal for use in industries such as food processing, oilfield piping and heat exchangers, and flue gas desulfurization.

The flange is second most used joining method after selding. Flanges are used when joints need dismantling. It provides flexibility for maintenance. Flange connects the pipe with various equipment and valves. Breakup flanges are added in the pipeline system if regular maintenance in required during plant operation.
A flanged joint is composed of three separate and independent although interrdlated components; the flanges, the gaskets, and the bolting; which are assembled by yet another influence, the fitter. Special controls are required in the selection and application of all there elements to attain a joint, which has acceptable leak tightness.
A flange is a protruded ridge, lip or rim, either external or internal, that serves to increase strength (as the flange of an iron beam such as an I-beam or a T-beam); for easy attachment/transfer of contact force with another object (as the flange on the end of a pipe, steam cylinder, etc., or on the lens mount of a camera); or for stabilizing and guiding the movements of a machine or its parts (as the inside flange of a rail car or tram wheel, which keep the wheels from running off the rails). The term “flange” is also used for a kind of tool used to form flanges.

Duplex 2205 stainless steel (ferritic and austenitic) is widely used in applications requiring good corrosion resistance and strength. Grade S31803 stainless steel was modified several times to form UNS S32205, which was recognized in 1996.

The material has high strength values. The minimum yield strength is 450MPa and the minimum tensile strength is 620MPa, with 25% minimum elongation and 290HB Brinell hardness.

S31803 stainless steel is a nitrogen alloy duplex stainless steel containing 22% chromium, 3% molybdenum, and 5-6% nickel. In addition to high strength and excellent impact toughness, it also has high resistance to general corrosion, localized corrosion and stress. Corrosive properties.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.61

The high chromium, molybdenum, and nickel levels provide excellent resistance to pitting, crevice, and general corrosion.

UNS S32205 nuts (also known as S31803) are manufactured from high-grade duplex 2205 stainless steel. Since this material is composed of at least 22% chromium, 6% nickel and 3% molybdenum it can withstand several unique types of environmental inflexibilities that other metals cannot such as corrosion, cracking, erosion, pitting and more. Super duplex stainless steel 2205 nuts also provide twice the mechanical strength compared to standard stainless steel.

The combination of chromium, molybdenum and nitrogen gives 2205 good resistance to chloride pitting and crevice corrosion. This resistance is extremely important for services such as marine environments, brackish water, bleaching operations, closed loop water systems and some food processing applications.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.53

2205 helps users to avoid stress corrosion cracking that is typically seen with 316 and 317.

At temperatures above 300¡ãC, the brittle trace components of 2205 precipitate, and at temperatures below -50¡ãC, the trace components undergo a ductile-brittle transition; therefore, this grade of stainless steel is not suitable for use at these temperatures.

A ferrous metal is one that contains iron. Therefore, stainless steels are ferrous metals as their main constituent is iron, even in the very highly alloyed grades, such as super duplex stainless steels, or super austenitic stainless steels.
Type “Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size “OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”

The advantage of the dual-phase structure is that it combines the advantages of ferritic alloys (resistance to stress corrosion cracking and high strength) with the advantages of austenitic alloys (ease of manufacture and corrosion resistance).

ASTM A182 F51 flanges refer to pipe flanges made from the forged duplex stainless steel grade UNS S31803 for use in pressure systems.

Compared with austenitic stainless steel, F51 duplex stainless steel has twice the compressive strength, and compared with 316L and 317L, the designer can reduce its weight.

2507 Duplex Plate also exhibit better ductility and toughness compared to ferritic stainless steels, but they do not provide these properties as successfully as austenitic stainless steels.

Alloy 2205 duplex stainless steel plate is an alloy duplex stainless steel plate containing 22% chromium, 3% molybdenum, and 5-6% nickel nitrogen.

A789 UNS S31803 and UNS S32205 are two grades of duplex stainless steel that are widely used in various industrial applications. These Duplex S31803 Seamless Pipes are known for their excellent corrosion resistance, high strength, and good weldability. A789 is a specification that covers seamless and welded tubes made from duplex stainless steel.

We are a manufacturer of Stainless Steel Round Bar, Formed Steel and Rebar, we supply bars such as 304, 304l, 316, 316l and 347. We are proud to have the largest share of stainless steel forming steel in the country.

Applications for duplex 1.4462 coated studs are the oil and gas industry, marine industry, chemical industry, paper and pulp industry, etc. We offer Lean Duplex and Standard Duplex in a wide selection of duplex grades. Duplex 2205 studs have specific properties for different environments. The chemical composition of the duplex 2205 material has chromium, nickel and molybdenum in the composition. Duplex 2205 studs are cost-effective and lower than other duplex grades and are in high demand.

La tuberia soldada ASTM A790 UNS S32205 se fabrica para obtener una resistencia adicional. Los tubos soldados se laminan en caliente, mientras que los tubos sin costura se estiran en frio.Ambos pueden reforzarse aun mas mediante el trabajo en frio, pero hasta cierto punto.

Duplex 2507 (UNS S32750) is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment.

The formation of ASTM A479 duplex steel UNS S32205 tie rod consists of a pool of austenite surrounded by continuous ferrite phases. ASME SA 479 Duplex Steel UNS S31803 Tie Rods are hot worked in the temperature range of 1750¡ãF to 2100¡ãF. This is designed to reduce the depth used in fabrication, thereby reducing the weight of precise significance for items such as pressure vessels, structural functions, etc. As ASTM A479 dual phase steel for bridges, storage tanks, etc. UNS S32205 rebar has approximately twice the superior performance of SS 304 .

In order to convey the pipeline, it is necessary to remove the straight hose in the pipeline. When using various pipelines, various pipelines must be used. When the pipeline is used, the elbow must be used to change the size of the pipeline. When bifurcating, the three-way pipe The flange connection used when the joint is used with various pipe joints, in order to reach the long-distance transmission pipeline, in order to reach the thermal expansion and cold contraction joint or effective connection aging of the pipeline, the long-distance expansion and cold contraction joint is used for the connection of the pipeline. , In the connection of various instruments, there are also the connectors and plugs of the instrument phase.

Alloy 2205 UNS S32305/S31803 is a 22% chromium, 3% molybdenum, 5-6% nickel, nitrogen alloyed Duplex Stainless Steel Pipe with high general, localized, and stress corrosion resistance properties in addition to high strength and excellent impact toughness.
Type “Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size “OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”