High Quality hex bolt as per DIN931 933 Bolts A194 2H hex bolt alloy bolt

Common Trade Names: Nickel Alloy 36, Invar 36®, Nilo 6®, Pernifer 6®
Invar 36® is a nickel-iron, low expansion alloy that contains 36% nickel, Invar 36 has a low coefficient of expansion from cryogenic temperatures to about +500°F (260°C).
Invar 36 Tube OD:0.2-6mm, WT: 0.02-2mm

Nilo / Alloy K W.Nr.: 1.3981
UNS: K94610 ASTM F15
Fixed-expansion glass-encapsulated iron-nickel-cobalt alloys, Kovar alloys, have a linear thermal expansion coefficient similar to that of hard glass within a certain temperature range
For mating sealing with hard glass

Nilo Alloy 36, W.Nr 1.3912, Invar 36® is a nickel-iron, low controlled expansion alloy that contains 36% nickel and possesses a rate of thermal expansion approximately one-tenth that of carbon steel.
Invar 36 Specifications: UNS K93600, W.Nr 1.3912

While each variation of Inconel has unique traits that make it effective in different circumstances, the majority of the alloys are used frequently in the chemical industry.Its welding characteristics,
especially its resistance to postweld cracking, are
outstanding

All chrome molybdenum steel sheets are sedated and heat treated in accordance with ASTM A387, which also specifies minimum and maximum levels of the following elements in steel: Chemicals of Carbon, Manganese, Phosphorus, Sulfur, Silicon, Chromium, Molybdenum, Nickel, Vanadium requirements, columbium, boron, nitrogen, aluminum, titanium and zirconium. A387 boards must undergo product, chemical and tensile testing (documented in the MTC or material test certificate) – must meet specific requirements for tensile strength, yield strength and elongation.

ASTM A335 grade P91 tubing contains small amounts of other alloys such as aluminum, niobium, nickel, nitrogen, titanium, vanadium, and zirconium. These pipes are based on the A335 standard, but when forged or drilled, the pipes can also meet the A369 standard. These pipes have a minimum yield strength of 415 MPA and a minimum tensile strength of 585 MPA.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.30

We have many years of experience in manufacturing ASME SA335 grade P9 alloy seamless steel pipe and provide high quality, low cost but best service.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.27

These are used in applications where the resistance required is not much and general corrosion resistance is required.

ASTM A182 Grade F5 Flanges are suitable for connecting pipes of small bore size and without the requirement of welding. ASTM A182 GR F5 Flange belongs to the ASTM A182 specification. The dimensions of the flanges vary according to the ANSI, ASME and DIN standards. The flange sizes range from ? inches to 36 inches in nominal bore sizes. Navstar Steel is a leading supplier and manufacturer of these flanges in various sizes and types.

A193 B7 threaded rods are also known as hex bolts. It has threads on both ends and it is a relatively long rod.

Our Alloy Steel Flanges are widely used in various industrial applications.

Due to the chemical composition of Molybdenum (Mo) and Chromium (Cr), A335 is often referred to as Chromium Molybdenum Tube. Molybdenum increases the strength of the steel as well as the elastic limit, wear resistance, impact quality and hardenability. Molybdenum increases resistance to softening, inhibits grain growth, and makes chromium steel less susceptible to embrittlement. Molybdenum is the most effective single additive for improving high temperature creep strength. It also enhances the corrosion resistance of the steel and inhibits pitting corrosion. Chromium (or chrome) is the basic component of stainless steel. Any steel with 12% or more chromium is considered stainless steel. Chromium is almost irreplaceable in terms of resistance to oxidation at high temperatures. Chromium increases tensile, yield and hardness at room temperature.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19
Material Alloy Steel ASTM A333 Grade 3, Grade 6,Grade 8,Grade 9
ASTM A335 P5,P9,P11,P12,P22,P91,P99

The production of ASME SA182 F9 flanges will be done using alloys with lower carbon content. Reducing the carbon content in these alloys reduces the formation of carbide precipitates. This basically means that alloy steel F9 flanges will no longer be susceptible to intergranular corrosion in the heat affected weld zone.

Although blind flanges and certain reducing flanges could include plate as a material for construction.

ASTM A335 P11 pipe (ASME SA335 P11) is a chromium-molybdenum alloy seamless pipe for high temperature service. P11 grade pipe has a chromium content of 1.00% to 1.50%, a molybdenum content of 0.44% to 0.65%, and a minimum tensile strength of 415MPa. Minimum yield strength 205Mpa.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19
Material Alloy Steel ASTM A333 Grade 3, Grade 6,Grade 8,Grade 9
ASTM A335 P5,P9,P11,P12,P22,P91,P131

In order to strengthen chromium alloy flanges, elements such as copper, titanium, vanadium and niobium are added to the alloy.

ASTM A182 Gr F9 flanges are typically designed for applications with high temperature requirements. Alloys used to produce flanges according to this specification include wrought or rolled alloys and several stainless steel grades.

Seamless pipes are used with slip on flanges to make the process smooth. The Alloy Steel Blind Flanges are used to close a pipe connection.

Applications for Alloy Steel A335 P5 EFW Tubing can be seen in petrochemical, oil and gas industrial applications, power plants and other high pressure and high temperature services.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19
Material Alloy Steel ASTM A333 Grade 3, Grade 6,Grade 8,Grade 9
ASTM A335 P5,P9,P11,P12,P22,P91,P123

A182 F9 flanges also contain carbon, manganese, silicon, phosphorus, sulfur, molybdenum and 8% chromium in their composition. This combination provides the joint with a minimum tensile strength of 585MPa and a minimum yield strength of 380MPa.

Pipe to ASTM A335 P11 can be cold drawn or hot rolled. Each tube shall be reheated for heat treatment – fully or isothermally annealed, normalized and tempered at a temperature not lower than 1200¡ãF (650¡ãC). Each pipe length shall be hydrostatically tested to ASTM A335 P11, along with dimensional inspection and visual inspection. Longitudinal or transverse tensile tests, flattening tests or bending tests are carried out for each heat.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19
Material Alloy Steel ASTM A333 Grade 3, Grade 6,Grade 8,Grade 9
ASTM A335 P5,P9,P11,P12,P22,P91,P129

ASTM A194 Grade 2H bolts are high strength bolts made from carbon steel.

A182 alloy flange has good dimensional accuracy.

The minimum yield and tensile strength requirements for ASTM A193 Grade B7m bolts are reduced compared to Grade B7 bolts. ASTM A193 B7 heavy duty hex bolts are readily available in the market. Therefore, A193-B7 studs are used in many applications due to their easy availability. ASTM A193 B7 Studs are commonly used in pipe flange connections and construction.

Our alloy steel ASTM A182 F5 butt weld flanges can be used in auxiliary industrial high pressure services such as condensers, boilers, evaporators, heat exchangers and more.

ASTM A182 F9 flanges are more versatile. This flange is thinner in size, easy to install in tight working spaces, and more economical compared to various other flanges.

Its tensile strength is 380 Mpa, while its yield strength is 585 Mpa at 0.2% Offset. The elongation of astm a182 gr f9 is 20 %.

These Alloy F5 Flange are used for transferring liquid and other fluids to several industries. We are manufactured by a team of nimble-fingered professionals using high quality raw material, modern tools and advance technology.

ASTM A182 F11 Alloy Steel Flanges are used in manufacturing of flanges and fittings and are used in industries where cold temperature is observed and corrosion resistance doesn¡¯t matter much.

A182 Gr F1 threaded flange is widely requested, also known as threaded flange, it has a thread in the flange hole, it is installed on the pipe, it matches the external thread on the pipe.

The Chromoly based F12 material specification are ideal for applications, where the piping systems are to transport or carrying corrosive fluids or gases at high-temperatures. Alloy Steel F12 Flanges they are used in various applications. Applications include chemical equipment, pharmaceuticals, gas processing plants, power generation tools, petrochemical industry, pulp and paper industry, on shore and offshore marine equipment, oil rigs, oil refineries, under water equipment, water desalination plants, condensers, heat exchangers and others.

The flanges also come in B16.5, B16.47 and other standards and dimensions. The Alloy Steel Flange Material can vary according to the chemical composition.

A194 2H Heavy Duty Hex bolts are designed for high strength, high temperature or high pressure applications and are usually available in a plain finish.