Din2527 Astm A105 Flange Wn Ac A694 Gr F65 600 Rf Blind Asme B16.5

Common Trade Names: Nickel Alloy 36, Invar 36®, Nilo 6®, Pernifer 6®
Invar 36® is a nickel-iron, low expansion alloy that contains 36% nickel, Invar 36 has a low coefficient of expansion from cryogenic temperatures to about +500°F (260°C).
Invar 36 Tube OD:0.2-6mm, WT: 0.02-2mm

316L 1.4401 S31603 Stainless Steel Pipe is a highly versatile and durable pipe option commonly used in a wide range of industrial and commercial applications. This SS UNS S31603 pipe is made from high quality 316L stainless steel with excellent resistance to corrosion, oxidation and staining, making it ideal for harsh environments or high stress applications.

Inconel 600 round bar is a nickel-based alloy with benign carburization and excellent corrosion resistance at high temperatures. Inconel 600 round bars are effective against drying Cl2 and many other different gases at mild and high temperatures. Alloy 600 bar is a nickel-chromium alloy with good oxidation resistance and resistance to chloride pressure decomposition cracking, high cleanliness water corrosion and acid oxidation at elevated temperatures.

Hastelloy C2000 Tubes are used in a broad range of industries including petrochemical processing, chemical processing equipment manufacturing, oil refineries and power plants.

It demonstrates good resistance to neutral and reducing environments. This alloy creates a tenacious oxide, protective film that does not spall off, but it retains superior oxidation resistance at soaring temperatures.

It is widely used in offshore oil and gas exploration/production and in heat exchangers in petrochemical/chemical processing.

It is able to withstand a wide range of oxidizing and non-oxidizing chemicals, and exhibits outstanding resistance to pitting and crevice attack in the presence of chlorides and other halides.

Nilo / Alloy K W.Nr.: 1.3981
UNS: K94610 ASTM F15
Fixed-expansion glass-encapsulated iron-nickel-cobalt alloys, Kovar alloys, have a linear thermal expansion coefficient similar to that of hard glass within a certain temperature range
For mating sealing with hard glass

AL6XN is a superaustenitic stainless steel with outstanding resistance to chloride pitting, crevice corrosion and stress corrosion cracking. AL6XN is a 6 moly alloy that was developed for and is used in highly aggressive environments. It has high nickel (24%), molybdenum (6.3%), nitrogen and chromium contents that give it excellent resistance to chloride stress corrosion cracking, chloride pitting, and exceptional general corrosion resistance. AL6XN is primarily used for its improved pitting and crevice corrosion resistance in chlorides. It is a formable and weldable stainless steel.

Nickel 200 flanges The Nickel 200 Flanges are durable, dimensionally stable, and have a fine finish. Moreover, the ASTM B564 UNS N02200 Blind Flanges are resistant to corrosion in neutral and oxidizing environments, making them perfect for use in food handling equipment.

This provides greatly enhanced resistance to sulfuric acid. It also has a high chromium content, to maximize its resistance to oxidizing chemicals and process streams contaminated with ferric ions and dissolved oxygen.

Hastelloy C2000 is available in a variety of sizes and thicknesses, this type of nickel-chromium-molybdenum alloy is renowned for its superior strength and corrosion resistance.

SCH40 Monel 400 Pipe is designated as Werkstoff Number 2.4360 and UNS N04400. Alloy 400 Pipe also known as Monel Alloy 400 Pipe, Monel 400 Pipe & Nickel Alloy 400 Pipe.

SMO 254 Pipes can withstand high mechanical stress and Alloy 254 SMO Pipe high pressure work in high temperatures and corrosive environments.

Higher chromium, molybdenum and nitrogen content results in a Pitting Resistance Equivalent Number (PREN) > 40, providing superior pitting and crevice corrosion capabilities to austenitic and duplex stainless steels in virtually all corrosive media, and critical pitting temperature Above 50¡ãC .

The 316 stainless steel pipe has become an indispensable material for the industrial sector. This alloy of iron and chrome is recognized for its high resistance to corrosion, as well as its durability. 316 stainless steel tubing can be produced in both seamless and welded tubes to meet specific customer needs.

Nickel Alloy 400 and Monel 400, also known as UNS N04400, is a ductile nickel-copper-based alloy consisting primarily of two-thirds nickel and one-third copper. Nickel Alloy 400 is known for its resistance to a variety of corrosive conditions, including alkalis (or acids), salt water, hydrofluoric acid, and sulfuric acid. Since Monel 400 or Alloy 400 is a cold worked metal, this alloy has high hardness, stiffness and strength. By cold working ASTM B164 UNS N04400 bar stock, the alloy is subjected to higher levels of mechanical stress, which in turn causes changes in the alloy’s microstructure.

Nilo Alloy 36, W.Nr 1.3912, Invar 36® is a nickel-iron, low controlled expansion alloy that contains 36% nickel and possesses a rate of thermal expansion approximately one-tenth that of carbon steel.
Invar 36 Specifications: UNS K93600, W.Nr 1.3912

The pipes of seamless configurations have higher load-bearing capacity and strength over other grades.

Nickel-copper-based alloy 400 Monel 2.4360 cold drawn rod is virtually immune to chloride stress-related corrosion cracking when exposed to corrosive media in typical environments. Monel 400 is a copper and nickel based alloy that is popular today due to its high performance. The alloy has excellent acid and alkali resistance. In addition, it has good tensile strength, ductility, excellent thermal conductivity, and can be hardened by cold work. Additionally, it can be used in applications with temperatures ranging from minus to 538 degrees Celsius.

Titanium’s density is about 60% that of stainless steel and nickel alloys, this weight saving makes it a popular choice in applications where this is critical such as aerospace.

Hastelloy Alloys Directory
The Corrosion Resistant HASTELLOY alloys are widely used by the chemical processing industries. The need for reliable performance leads to their acceptance and growth in the areas of energy, health and environmental, oil and gas, pharmaceutical and flue gas desulfurization industries.

Alloy 800 is a nickel-iron-chromium alloy with high strength and excellent resistance to oxidation and corrosion at high temperatures. ASTM B407 UNS N08800 Incoloy 800 W. Nr. 1.4876 Welded Pipe is widely used for construction of equipment requiring corrosion resistance, heat resistance, strength, and stability for service up to 1500°F (816°C).

Alloy 800 Weld Neck Flanges We have a strong reputation in the industry for producing high-quality flanges of different types that would suit the requirements of our clients. We manufacture Incoloy 800 Flanges which are reliable and high in quality. We use premium resources and advanced machinery for producing ASTM B564 UNS N08800 Incoloy 800 Flanges.

UNS N08367 also commonly referred to as alloy AL6XN is a low carbon, high purity, nitrogen-bearing “super-austenitic” nickel-molybdenum alloy with excellent resistance to chloride pitting and crevice corrosion.

Incoloy 800H Flange We have a strong reputation in the industry for producing high-quality flanges of different types that would suit the requirements of our clients. We manufacture Incoloy 800 Flanges which are reliable and high in quality. We use premium resources and advanced machinery for producing ASTM B564 UNS N08800 Incoloy 800 Flanges.

Nickel based 800 Incoloy Hexagonal Pipe is known to have a good resistance to corrosion. Specifically speaking, the Incoloy 800 Pipe offers sufficient resistance against both carburization as well as oxidation corrosion.

Inconel 625 Coil is characterized by its excellent resistance to oxidation, high-temperature corrosion and fatigue. ASTM B443 UNS N06625 Inconel Plate is widely used in the aerospace, chemical processing and oil and gas industries due to its superior strength, toughness and durability even in extreme environments.

Inconel 600 seamless tubes of standard UNS N06600 and ASTM B167 are the ones manufactured to sustain excessively high pressure and come with great warranty.

A335 P5, P9, P11, P12, P22, P91 grade alloy steel seamless pipes are individually sheathed in plastic bags, and the pieces are made of waterproof packaging material and tied with nylon ropes. There is a clear label on the outside of the package for easy identification of quantity and product ID with great care during handling and shipping.

ASTM A182 F321 is a forging material specification for 321 grade stainless steel and is used for manufacturing bare forgings or forged and machined products for applications involving high temperature service.

Pure titanium is almost 99.2% pure and is a lustrous metal with low density and high corrosion resistance.

The specification for standard ASTM A182 F9 Flanges covers both forged or Rolled Alloy Steel Pipe Flanges & Fittings, that have been designed and manufactured for high temperature service. ASTM A182 F9 Flanges have a minimum chromium content of 18% in the alloy. This makes it survive in temperatures up to 870 degrees Celsius.

Inconel 718 round bar is a nickel-chromium alloy bar with up to 55% nickel in its composition. Contents include 17% chromium, 4.9% niobium, 6.6% iron minimum and aluminum, boron, carbon, cobalt, copper, manganese, phosphorus, lead, sulfur and silicon. The material has an ultimate tensile strength of 1375 MPa and a minimum yield strength of 1100 MPa.

These pipes can be hot or cold-rolled to get desirable properties. The Polished 304 Stainless Steel Pipe provides a smooth finish and increased resistance to steel pipes.
Type “Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size “OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”

Grade 316, and grade 304, may suffer stress corrosion cracking in solutions containing chloride ions at temperatures over about 60¡ãC. Stress corrosion cracking should be considered for all corrosion services where the corrosive liquid may contain chloride.

Alloy steel DIN 1.7335 round bars also offer some other outstanding properties such as perfect finish, dimensional stability, light weight, high load-carrying capacity, longer life, fine dimensions and more.

The nickel content of Alloy 825 makes it resistant to chloride stress-corrosion cracking, and combined with molybdenum and copper, provides substantially improved corrosion resistance in reducing environments when compared to conventional austenitic stainless steels.

In terms of mechanical properties, the alloy 601 flange has a minimum tensile strength of 550MPa, a minimum yield strength of 205MPa and an elongation of 30%. The material is denser than ordinary stainless steel and has a melting point of 1411 degrees Celsius. These flanges belong to the ASTM B564 specification, and the standards include ASME, ASTM, DIN and other international standards such as ASME B16.5, B16.47, etc.

The key elements in 304 are chromium and nickel, which give it excellent corrosion resistance. It has good corrosion resistance, is ductile and ductile, and has good weldability. The austenitic structure allows deep drawing without intermediate annealing.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.39

Stainless steel flanges will not be corroded, pitted, rusted or easily worn, and it has excellent service performance, it will stand out among many flanges.

Type 316 stainless steel tubing is similar to 304, but with the addition of molybdenum, which improves the alloys corrosion resistance. The austenitic structure allows excellent toughness, even down to extremely low temperatures. These grades have excellent weldability, with or without the addition of filler metal.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.20

Inconel Alloy 600 tubing is made from a non-magnetic, nickel-chromium alloy known for its good oxidation resistance at high temperatures. In fact, Inconel Alloy 600 (UNS N06600) was designed for use from cryogenic to elevated temperatures up to and surpassing 2000 degrees F. Inconel Alloy 600 tubing possesses great mechanical properties, a good combination of high strength with good workability, and is weldable without difficulty. Inconel? Alloy 600 is not precipitative hardenable, it is hardened and strengthened solely through cold work.

In order to convey the pipeline, it is necessary to remove the straight hose in the pipeline. When using various pipelines, various pipelines must be used. When the pipeline is used, the elbow must be used to change the size of the pipeline. When bifurcating, the three-way pipe The flange connection used when the joint is used with various pipe joints, in order to reach the long-distance transmission pipeline, in order to reach the thermal expansion and cold contraction joint or effective connection aging of the pipeline, the long-distance expansion and cold contraction joint is used for the connection of the pipeline. , In the connection of various instruments, there are also the connectors and plugs of the instrument phase.

Inconel 625 alloy is used for heat shields, furnace hardware, gas turbine engine ducting, combustion liners and spray bars, chemical plant hardware and special seawater applications.

ASTM Specification A106 covers seamless carbon steel nominal wall pipe for high-temperature service, suitable for bending, flanging and similar forming operations. NPS 1-1/2 and under may be either hot finished or cold drawn. NPS 2 and larger shall be hot finished unless otherwise specified. Surface finish standards are outlined in the specification.

C276 is forged between 2250/1750oF (1230/955oC) and then soaked at the forging temperature for 30 minutes per inch of billet or ingot section thickness. Forging should begin immediately, the billet is removed from the reheat furnace, a 25/40% reduction helps retain as much internal heat as possible. For optimum corrosion resistance, forged parts should be subsequently annealed. See Heat Treatment.

For maximum corrosion resistance, forgings should be annealed at 1900°F minimum and water quenched or rapidly cooled by other means after hot working operations.

ASTM A320 Class L7 fasteners are manufactured using high strength materials ideal for the manufacture of fastener product bolts, studs and bolts that can be used in a wide range of high temperatures in bolting applications.

Incoloy 800H Flange Incoloy 800 / 800H / 800HT Flanges are furnished with nickel-chromium-iron alloys that intend outstanding resistance and strength at harsh environments. The flanges exhibit superior resistance to chloride stress corrosion cracking and crevice corrosion. Even more, it also shows superior intergranular corrosion, stress rupture and creepy aspects. The welding of these flanges is done using various techniques such as MIG, TIG and more.

ASTM A479 UNS S32750 / A182 F53 Stud Bolts, which is a threaded rod with two heavy hexagon nuts. In the petroleum and chemical industry, these Super Duplex ASTM A479 UNS S32750 Stud Bolts is the most common bolt used for flanged connections.

Within in these critical industries you can find Nickel Alloy 625 and Inconel 625 in various applications including:Nuclear reactor-cores and control-rod components, Wire rope for cables and blades on Naval crafts such as gunboats and subs, and Oceanographic equipment etc.

There are different pressure classes of these flanges ranging from Class 150 Monel UNS N04400 Flanges to class 2500, and PN6 to PN64.

Titanium is a dimorphic element with a hexagonal form that slowly converts into a body-centered cube at an elevated temperature of 880 ?C.

A182 F9 flanges also contain carbon, manganese, silicon, phosphorus, sulfur, molybdenum and 8% chromium in their composition. This combination provides the joint with a minimum tensile strength of 585MPa and a minimum yield strength of 380MPa.

SS 316/316L flanges can be fabricated from ASTM A182 F316 or F316L forgings, ASTM A351 CF8M or CF3M castings, and ASTM A240 316 or 316L plates per ASME B16.5 and ASME B16.47.

Stainless steel 316/ 316L flanges can be made by hot forging or casting. Blind or sliding plate flanges without hubs can be machined directly from the plate. Flanges should be solution treated at not less than 1900¡ãF [1040¡ãC] and then quenched in cold water or other rapid cooling method.

The reason for alloy grade 304 Stainless Steel 304 Pipes being popular is that it offers good resistance to corrosion in several mediums. This is due to a higher content of chromium used in the alloying of stainless steel pipes 1.4301.
Type “Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size “OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”

Steel flanges provide an easy access for cleaning, inspection or modification. They usually come in round shapes but they can also come in square and rectangular forms. The flanges are joined to each other by bolting and joined to the piping system by welding or threading and are designed to the specific pressure ratings; 150lb, 300lb, 400lb, 600lb, 900lb, 1500lb and 2500lb.

A flange can be a plate for covering or closing the end of a pipe. This is called a blind flange. Thus, flanges are considered to be internal components which are used to support mechanical parts.