ASTM A286 UNS S66286 round Bar
A286 stainless steel Chemical Composition
| Element |
Content (%) |
| Iron, Fe |
54 |
| Nickel, Ni |
25.5 |
| Chromium, Cr |
14.8 |
| Titanium, Ti |
2.13 |
| Molybdenum, Mo |
1.30 |
| Manganese, Mn |
1.0 |
| Silicon, Si |
0.50 |
| Vanadium, V |
0.30 |
| Aluminum, Al |
0.18 |
| Carbon, C |
0.040 |
| Phosphorous, P |
0.020 |
| Sulfur, S |
0.015 |
| Boron, B |
0.0060 |
A286 stainless steel Physical Properties
| Properties |
Metric |
Imperial |
| Density |
7.92 g/cm3 |
0.286 lb/in3 |
| Melting point |
1399°C |
2550°F |
Stainless steel grade 660 Mechanical Properties
A286 Stainless Steel Yield Strength
| Properties |
Metric |
Imperial |
| Tensile strength |
1035 MPa |
150100 psi |
| Yield strength (@strain 0.200%) |
759 MPa |
110000 psi |
| Elongation at break |
25% |
25% |
| Reduction of area |
40% |
40% |
| Hardness, Brinell (estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball) |
304 |
304 |
| Hardness, Knoop (estimated from Rockwell C value) |
330 |
330 |
| Hardness, Rockwell C |
32 |
32 |
| Hardness, Vickers (estimated from Rockwell C value) |
318 |
318 |
.jpg)