Super Duplex S32760Download

 Super Duplex S32760
Our stock of Super Duplex 32760 can be supplied in sheet, plate, or bar forms, cut to specific requirements and comes with the Jain Steels Metal quality certification.

The following are the properties of S32760 Super Duplex:
 Ferritic-austenitic stainless steel.
 Excellent corrosion resistance against general corrosion, stress corrosion cracking, corrosion fatigue, pitting, crevice and erosion corrosion and possessing very high mechanical strength properties.
 Good weldability, post weld heat treatment not necessary.
 Max. Temperature for long periods of service: 280°C (536°F) / (300°C/572°F possible for short periods).
 Surface condition for optimum corrosion resistance: pickled or machined.

Application
Components in offshore, waste water, sea water desalination and chemical plants with aggressive chloride-containing media e.g. heat exchangers, separator parts, compressor and pump components, turbine blades.
Technical Info
Chemical Composition (average %)

C

Si

Mn

Cr

Mo

Ni

W

Cu

N

PREN

0.020

0.25

0.55

25.20

3.70

7.00

0.65

0.60

0.22

Min. 40

Standards UNS S32760

Hot Forming
Forging
1280 to 1000°C (2336-1832°F)
Air cooling

Heat Treatment
Quenching:
1100°C (2012°F)
Water , air (thickness below 2mm)
Structure as quenched:
1100°C (2012°F)
Water , air (thickness below 2mm)
Structure as quenched:
Ferrite + Austenite

Welding
Weldability of super duplex 32760 is good. The welding procedures are similar to those applied for conventional duplex grades. Welding consumables for different welding methods are available.

Machining
The machine ability of super duplex 32760 is superior to comparable super duplex grades due to its optimised inclusion characteristic. Further details are available on request.

Mechanical Properties
Condition: quenched

Product

Dimension
Size
mm

0.2% proof stress
N/mm2
min.

Tensile strength
N/mm2
min.

Elongation A5
% min.
L    Q     T

Impact strength
(ISO-V)
J min.
L    Q     T

St, Sch

≤250

550

750

25   – –    – –

70   – –    – –

Bl

≤ 75

– –   251)  – –

– –   55    – –

St = Bar , Sch = Forging,
Bl = Sheet or plate
L = Longitudinal, Q = Transverse, T = Tangential
1) < 3mm = A80mm specimen
The values for other products and dimensions shall be established by agreement.

Hight Temperature Properties
Condition: quenched

0.2% yield strength
N/mm² min.

Temperature

50°C (122°F)

100°C (212°F)

150°C (302°F)

200°C (392°F)

250°C (482°F)

300°C (572°F)

510

480

445

405

400

395


Physical Properties
Thermal conductivity at …………….. 20°C (68°F) …………..15.0 …………W/(m.K)
Specific heat at ………………………..20°C (68°F) …………..450 ………….J/(kg.K)
Electrical resistivity at ………………. 20°C (68°F) …………..0.80 …..Ohm.mm2/m
Modulus of elasticity at …………….. 20°C (68°F) …………..250 x 103 …N/mm2
Magnetic properties …………………………………………………magnetic

20°C und …°C, 10-6 m/(m.K) bei
Thermal expansion between
20°C (68°F) and …°C (°), 10-6 m/(m.K) at

Temperature

10-6 m/(m.K)

˚C

˚F

100°C

212°F

13.3

200°C

392°F

13.6

300°C

572°F

14.0

400°C

752°F

170

Modulus of elasticity, 103 N/mm2 at

Temperature

103 N/mm2

˚C

˚F

20°C

66°F

205

100°C

212°F

200

200°C

392°F

195

300°C

572°F

180

400°C

752°F

170

As regards applications and processing steps that are not expressly mentioned in this product description/data sheet, the customer shall in each individual case be required to consult us.